Achieving outstanding mechanical/bonding performances by epoxy nanocomposite as concrete

Blog

HomeHome / Blog / Achieving outstanding mechanical/bonding performances by epoxy nanocomposite as concrete

Jul 15, 2023

Achieving outstanding mechanical/bonding performances by epoxy nanocomposite as concrete

Scientific Reports volume 13, Article number: 9157 (2023) Cite this article 659 Accesses 3 Citations Metrics details Anchoring steel rebar in concrete structures is a common method in the building and

Scientific Reports volume 13, Article number: 9157 (2023) Cite this article

659 Accesses

3 Citations

Metrics details

Anchoring steel rebar in concrete structures is a common method in the building and construction industry. This research focuses on improving the mechanical/bonding properties of the prepared epoxy nanocomposite adhesive using surface treatment of SiO2 nano fillers by glycidoxypropyltrimethoxysilane (GPTMS). For this purpose, the nano silica particles were silanized via a facile sol–gel method at silane concentrations of 1, 5, 10 and 20X (i.e. X is stoichiometric silane concentration). The nanoparticles were characterized carefully by FTIR, TGA, XRD and XPS techniques. It was found that the highest GPTMS grafting ratio was obtained at silane concentration of 10X. The pure and silanized nanoparticles were added to a two-pack epoxy resin and were compared for tensile and compressive properties. It was found that surface modification of nano silica caused improvement in the strength, modulus, compressive strength and compressive modulus by 56, 81, 200 and 66% compared to the pristine epoxy adhesive and also 70, 20, 17 and 21% compared to the pure nano silica containing adhesive. It also caused 40 and 25% improvement in the pullout strength, 33 and 18% enhancement in the pullout displacement and 130 and 50% in adhesion energy compared to the pristine and raw silica-containing adhesives, respectively.

Concrete is one of the most valuable building materials that is found wherever there is an infrastructure1,2,3,4. Rebars, in the form of reinforcement, are used to network the foundation and columns5,6,7. Also, another one of their most important applications in the foundation is the implementation of rabbits to prevent construction joints in concrete8. To reinforce the concrete in the structures, the rebars are connected with wire, so that the anchor system is firmly placed in the concrete9,10.

The bond between cement and steel rebar plays an important role in the physicochemical behavior of the anchor system10,11. In general, cracks in concrete are engendered by tensile stresses, which can be resulted by over load, temperature changes, and shrinkage, and resulted in poor connections, rebar slippage, and anchor failure12,13. Many efforts have been performed to improve the adhesion of steel rebar in cement concrete, including application of polymeric materials on the rebar surface (e.g. coatings14, epoxy resins15, etc.) and modifying the concrete mix design (e.g. with nanoparticles16, fibers17, etc.).

Generally concrete adhesives are divided into two types: epoxy based and latex/polymer based18. This kind of materials are used to repair concrete, seal concrete, increase the physicochemical properties of concrete, and connect old concrete to new one19. Some of the advantages of structural adhesives are strengthening the structure and augmenting the connection between materials, using in wet environments, connecting members with a cross-section, corrosion resistance and quick and easy implementation20,21. Planting rebar or bolt is one of the most commonly used methods in the construction industry. This includes a wide range of structural and non-structural connections as well as strengthening of the structures22,23. From this starting point, improving adhesive properties is the most efficient technique to prevent structural damages using strengthening the metal-to-concrete bonding24.

Nowadays, epoxy-based adhesives are of the most popular adhesives for steel rebar anchoring systems, due to their high adhesion strengths, fast and excessive compaction, impermeability against moisture, seawater, sewage and petroleum materials, significant resistance to vibrations and structural stresses and high mechanical properties19,25.

From 1980 onwards, researchers such as Bloxham26, Van Gemert et al.27 and Swamy et al.28 conducted studies on the reinforcement of concrete with steel rebar using epoxy adhesives.

Many scientists have investigated the mechanical and chemical behavior between adhesive bars and concrete29,30. It has been determined that the rebar with a larger diameter has higher failure in the connection with concrete, which in order to have a better connection and no brittleness, the length of the rebar should be fifteen times the diameter of the rebar31,32.

Zhao et al.33 investigated the bonding of steel rebar to concrete structure using epoxy adhesive. It was reported that the adhesive had good bond strength to both rebar and concrete and the failure of the system occurred at the interfaces of the adhesive, but the ductility of anchoring system decreased using epoxy adhesive.

In recent years, fillers are used to improve the physical and mechanical properties of adhesives34,35,36,37,38. It has been shown that the type, size and properties of fillers have a great impact on the bonding strength of adhesive joints and stress transfer between concrete and steel rebar39. Szymanowski et al.40 investigated the effect of using tetragonal crystalline titanium oxide nanoparticles (TiO2) in adhesive and its effect on bonding strength in layered cementitious composite. The results showed that inclusion of 0.5 wt% of TiO2 nanoparticles to the adhesive increased its bonding properties, wear resistance, tensile strength and hardness. Ismael et al.41 used nano SiO2 and AL2O3 in cementitious composites reinforced by steel fibers. The results showed that the addition of nanoparticles led to an increase in the bond between steel and matrix especially at higher cement contents. Using Al2O3 nanoparticles also caused decline in cracking. May et al.42 used multiwall carbon nanotubes (MWCNTs) to reinforce diglycidyl ether epoxy resin by sol–gel method. The results showed that the presence of nanoparticles causes better adhesion properties and tensile strength (up to 28.5 MPa) of epoxy resin. Li et al.43 modified silica nanoparticles with polymethylhydrosiloxane (PMHS) through the sol–gel process and used it for surface modification of materials. The results showed that the created interfacial chemical bonds enhanced hydrophobicity of the surface. It was found that fillers and chemical coupling agents could strengthen the connection between concrete and steel rebar. The effect of micro and nano silica particles on epoxy adhesives was also investigated. It was found that silica micro particles and their particle size affects the mechanical properties of epoxy adhesive and bonding strength to steel bar. However, silica nanoparticles caused decline in the properties that this was attributed to the tendency of hydrophilic nanoparticles to agglomeration in organic matrix44.

Based on the literature review, it was found that using of nanoparticles in anchoring adhesive has been studied in few researches. Furthermore, in most cases just the bond strength between concrete and rebar has been investigated and the effects on the mechanical properties of adhesive and its relation to concrete-rebar adhesion have not been assessed.

On this basis, the silica nanoparticles was selected as cost-effective filler in this research. It was surface modified by sol–gel method using an epoxy based silane coupling agent at different concentrations. The silane grafting was assessed by FTIR, TGA, XRD, SEM and XPS analysis. The raw and surface modified fumed silica were applied to a two pack epoxy adhesive. The prepared pure and modified nanocomposite adhesives were evaluated for flexural and compressive properties. The best adhesives (based on the mechanical properties) were used for anchoring of steel rebar in concrete. FE-SEM Analysis was used for characterization of the fractured surfaces of the adhesive samples. Finally, the effects of pure and modified nanoparticles on the concrete-rebar adhesion performances were studied.

Nanya NPEL-128 epoxy resin (Taiwan) and Epikure F205 as curing agent were used as binder in this study. Fumed silica nanoparticles with an average primary particle size of 25–35 nm was used as reinforcing nano filler for epoxy adhesives. Glycidoxypropyltrimethoxysilane (GPTMS) (GLYMO, Evonic Company) was used surface modification of fumed silica. Absolute ethanol (99.98%, Merck, Germany) was used as solvent.

Firstly, the optimal amount of silane required to modify the surface of nanoparticles was calculated by the following stoichiometric relationship45,46,47,48:

where mGPTMS and MGPTMS are the mass of the GPTMS (gr) and the molecular mass of the GPTMS, respectively. NA and nOH are Avogadro numbers and the number of hydroxyl groups, respectively.

This value varied depending on the molecular mass of the GPTMS, the specific surface area (BET) of the fumed nanoparticles and the TGA data (see Section 1S in supporting information).

Scheme 1 represents the surface treatment process of fumed silica by GPTMS. For this purpose, 0.5 g of fumed silica were added to 70 g of ethanol and sonicated at 30 °C for 1 h. Afterward, the GPTMS (i.e. at the content that calculated by Eq. 1) was added to ethanol, water and acetic acid (at a weight ratio of 0.1:0.05) to hydrolyze the GPTMS. The optimal pH of the hydrolysis solution was determined by zeta potential analysis. At this point, the prepared suspension of fumed silica in ethanol was poured into a flask. The solution was stirred and added to the reactor dropwise during 30 min. Thereafter the solution was mixed for 4 h and centrifuged. The sediments were separated and washed three times with acetone to remove unreacted GPTMS molecules. Finally, the modified fumed silica were dried in an oven for 12 h at 90 °C for GPTMS condensation on the nanoparticles surface.

Surface treatment process of fumed silica by GPTMS.

To enhance grafting ratio, the nanoparticles were also modified at silane concentrations of 5X, 10X and 20X (see Table 1).

To prepare pristine epoxy adhesive, the hardener was added to resin part at weight ratio of 1:2. The mixture was gently stirred to inhibit air bubble creation.

To prepare nanocomposite samples, nanoparticle (i.e. the raw or modified fumed silica) was added to the resin part (at 0.5, 1, 3 and 5 wt%). For this purpose, the fumed silica were added to n-butanol and sonicated at 28 °C and 200 W (frequency of 40 kHz) for 1 h. The resulted suspension was added gently to the resin and mixed slowly at 350 rpm for 30 min. The suspension was applied gently to the resin and mixed slowly at 450 rpm and put in a vacuum oven to remove the solvent. To prepare pure and modifies epoxy adhesive samples (see Table 2), the curing agent was applied to the resins based part at weight ratio of 1:2 and mixed gently49, and placed in ambient conditions for 10 h. Thereafter, the solidified specimens were removed and placed in an oven at 100 °C for 5 h for post curing.

The purpose of this study is to prepare an epoxy adhesive for effective anchoring of steel rebar in concrete. For this purpose, the concrete at the water-to-cement (w/c) ratio of 1:1.89 was prepared (see Table 3). The prepared concrete was poured into the cylindrical molds (see Sect. 2S in supporting information). The plastic bar (1 cm in diameter and 10 cm in length) was used to form anchoring hole in the concrete without drilling. The filled molds were held in ambient conditions for 24 h. Thereafter, the samples were placed in the water for 28 days to be cured. After curing of the concrete specimens, the steel rebar (0.8 cm in diameter and 20 cm in length) was inserted in the center of the hole (with 10 cm length) and then adhesive was inserted into the gap (i.e. 0.2 cm thickness) between the steel rebar and concrete wall. The specimens were placed at ambient temperature for 14 days to be cured.

The mechanical properties of nanocomposites and pullout strength were determined using a SANTAM STM150 Universal machine. The tensile, flexural and compressive tests were performed at loading rates of 5, 2 and 1.3 mm/min based on ASTM D638, D790 and D695 test methods, respectively. Three specimens were tested for evaluating each mechanical property. The pullout test was performed under tension mode based on ASTM C900 test method. The adhered steel rebar-concrete sample was placed in a steel fixture as the rebar were kept using the upside grip and the fixture was kept constant using the downside grip. The test was performed at tension rate of 10 mm/min. the steel rebar would exit gradually from concrete during loading (see Sect. 3S in supporting information). Three specimens were tested for evaluating pullout adhesion of each sample.

The grafting efficiency of raw and modified fumed silica were determined by thermogravimetric analysis (TGA) (Mettler-Toledo Co., Switzerland). FTIR was done by a TENSOR 27 to identify the chemical structure of nanoparticles and GPTMS. XPS was performed by ESCALAB 250 system (ESЄA System, USA). The particle size and morphology of the raw and modified fumed silica were examined by Field Emission Scanning Electron Microscopy (FE-SEM) (Hitachi, Japan). The X-ray diffraction (XRD) of the raw and modified fumed silica was determined by Bruker AXS diffractometer D8 (Madison, Wisconsin).

Dynamic mechanical thermal analysis (DMTA) was used to investigate viscoelastic behavior of nanocomposite epoxies (Netzsch Co., Germany). The water contact angle (WCA) of the fumed silica was measured using (UI-1220LE-M-GL, IDS-Germany).

The particles surface charge at different pH was investigated by evaluation of Zeta potential. The more negative zeta potential indicates more negative charge on the nanoparticle surface, better stability and better dispersion in the aqueous solvent. On this basis, samples with different pH of 2, 5, 7 and 9 were prepared and their zeta potential was measured (see Fig. 1).

Zeta potential for nano silica in different acidic conditions.

The results indicated that at pH 7, the most negative charge of nano silica is achieved. This confirms the presence of a number of OH groups on the fumed silica surface which are ready to be silanized. On this basis, this pH was selected as the best condition for silanization step.

Figure 2a shows the TGA results for the silanized and raw silica. As shown in the figure, all the samples exhibit large weight loss in the first region, which was related to the removal of the adsorbed H2O. The weight loss of modified nanoparticles were greater than pure nano silica in this region because of more water absorption during silanization process. In the second region, all the modified nanoparticles presented large weight losses, which were related to the degradation of grafted GPTMS. The weight loss of raw silica in this region corresponded to the de-hydroxylation of the OH groups. The highest weight loss in this region was obtained for the silanized silica (i.e. NS-G-10X sample). On this basis, this sample was selected as the optimal silanized for future processes. Figure 2b exhibits FTIR spectrums of the raw and silanized silica nanoparticles. In the spectrum of raw silica, the peaks at 961, 1528 and 1630 cm−1 were attributed to the bending vibration of O–H. The broad peak around 3450 cm−1 was related to the stretching vibration of O–H group. On this basis, there are three different types of hydroxyl groups on the surface of nanoparticles including covalently bonded, physically adsorbed and double-base hydroxyl groups.

(a) TGA curves of raw silica and silanized silica, (b) FT-IR spectroscopy of GPTMS, raw silica and silanized silica.

For modified silica nanoparticles, the bending vibration peaks of OH group at 1630 cm−1 were disappeared and their peaks at 3450 cm−1 were weakened. This was attributed to consumption of surface OH groups during hydrolysis of GPTMS. Furthermore, the peaks at 1109, 805 and 475 cm−1 were related to asymmetric, symmetric and bending vibrations of Si–O–Si, respectively. The peaks at 2800–3000 cm−1 in the spectrum of GPTMS were related to stretching vibrations of the CH and CH2 groups. These peaks appeared again in the modified nanoparticles that confirm successful grafting of GPTMS molecules. In contrary, they were not seen in the spectrum of raw nanoparticle due to its inorganic nature. The peaks were intensified in the spectrum of modified nanoparticles at concentration of 10X that confirms higher GPTMS grafting ratio for this sample. The results were in good correlation with TGA findings. For convenience, the nanoparticles that modified at concentration of 10X is called modified nano silica (i.e. MNS) instead of NS-G-10X from now on. Table 4 shows the results of TGA.

XRD analysis was used to detect crystalline phase of the raw and modified nanoparticles (see Fig. 3). It is evident that the position of peaks has not been moved but the broad peak located at 22° shows that all the nanoparticles have amorphous structure. It was found that the surface modification of nanoparticles have not influenced their crystalline phase. The size of the crystals was also calculated according to the Scherrer equation48,50,51 that were 17.01 and 16.97 nm for raw and silanized silica. This result illustrates negligible reduction in the size of crystals after modification with GPTMS.

Characterization of raw and modified silica fume; (a) XRD and (b) XPS analysis.

The XPS spectrums of the raw and surface optimal silanized silica are shown in Fig. 3. Narrow-scan spectra of C1s, O1s, and Si2p were used to determine changes in the chemical environment of the surface elements. The results confirmed successful grafting of GPTMS on the nanoparticles surface due to the intensified indicator peaks. Moreover, the coexisting peaks of Si2p (102.8 eV) and Si2s (156.3 eV) in the pure sample were related to the silanol group in silica structure. However, in the modified sample these peaks intensified due to the condensation of silane molecules that formed silanol layer on the nanoparticles surface. The XPS data are listed in Table 5.

Figure 4 shows FE-SEM photography of raw and silanized silica. The pure SiO2 nanoparticles had sizes ranging from 25 to 30 nm. The agglomeration tendency of pure nano filler could be observed due to hydroxyl bonding between surface OH groups. After surface treatment of the silica with epoxy based GPTMS, the particle size reduced to 20–25 nm due to steric stabilization of grafted silanes.

FE-SEM photography of; (a1, a2) raw silica and (b1, b2) silanized nanoparticles.

The raw silica was added to the resin part at four different concentrations. The nanocomposites were molded to prepare tests specimens. After curing, the specimens subjected to tensile, flexural and compressive tests. Figure 5 shows the results.

(a) Tensile, (b) flexural and (c) Strength and modulus properties of the pure nano silica and (d) tensile, (e) flexural and (f) compressive properties of the modified nano silica contained epoxy nanocomposites at different percentages of nanoparticles.

Based on the results, samples that contained 1wt% of raw silica showed the highest tensile, flexural and compressive properties among the other nanocomposites. It was concluded that at higher loading contents of the pure nano filler, the agglomeration of particles occurred that caused decrement in the mechanical properties. This confirms results of FE-SEM analysis.

The modified nanoparticles was also added to the epoxy resin at 1 wt%. The results were also shown in Fig. 5. It was seen that the tensile properties increased. It was attributed to the better dispersion of the silanized silica fume in the epoxy matrix due to steric stabilization of the nanoparticles that prepared by hindrance of the grafted silane groups47,48. The silanized silica fume showed no effects on the flexural properties but caused considerably increment in the strength and modulus properties of epoxy sample. The results were in good correlation to the results of FE-SEM and XRD analysis.

Figure 6 shows FE-SEM images prepared from fractured surface of the nanocomposites at two magnifications (i.e. 10 µm and 500 nm). Big aggregates (i.e. with size of 100 nm–2.5 µm) was seen in the raw silica containing sample (see Fig. 7a). This was attributed to the hydrophilic nature of the silica fume that caused aggregation in the epoxy matrix. This indicates poor dispersion of hydrophilic silica fume in the epoxy matrix. After surface treatment of silica fume, considerable homogeneous dispersion and small-size aggregates (of up to 100 nm) were seen. This was attributed to the steric stability of the silica fume that was performed by grafted GPTMS. Besides, the river like lines increased in the fractured surface of modified nanocomposite that confirmed improved interactions between epoxy matrix and silanized nanoparticles37,46,48.

FE-SEM photography of; (a1, a2) raw and (b1, b2) modified epoxy nanocomposites.

Mechanical properties of nanocomposites; (a) Storage modulus and (b) Tan δ.

The dynamic-mechanical behavior of the nanocomposites and its relationship to the nanoparticle surface chemistry was investigated by DMTA analysis. Figure 7a shows the storage module curve in terms of temperature. The results showed that silanization of nanoparticles led to an increase in the storage modulus of the nanocomposite52. This should be attributed to the improved interfacial interactions between nanoparticles and epoxy matrix. This limits movement of the chains and increases stiffness of the matrix. The glass–rubber transition temperature (Tg) of the sample (derived from peak temperature of tanδ curve) showed slight increment that confirmed improved networking in the matrix due to attachment of nanoparticles to epoxy matrix (see Fig. 7b and Table 6)53.

It was also observed that the pure nanoparticles caused decline in the storage modulus of the epoxy polymer which confirmed weak interfacial interactions between the polymer matrix and pristine nanoparticles. This was related to the weak filler–polymer interfacial interactions47,53. However, it had no effect on the Tg and tan δ of the cured pristine sample. This was attributed to the high crosslink density of the cured resin and its brittle behavior.

The WCA of the pristine epoxy and nanocomposite samples was measured that results are shown in Fig. 8. It is clearly seen that inclusion of pure nano silica caused increase in the hydrophilicity of the epoxy sample. In contrary, the modified nanoparticles increased hydrophobicity of the epoxy nanocomposite even more than pristine epoxy. This was attributed to presence of propyl and ethyl groups in the GPTMS structure that counteracted the effect of hydrophilic epoxide groups.

Water contact angle of (a) pristine epoxy, (b) raw silica containing epoxy nanocomposite (1 wt%) and (c) modified nano silica containing epoxy nanocomposite (1 wt%).

Figure 9 shows the pull-out test results for the anchored steel rebar in concrete specimens by pristine epoxy adhesive and nanocomposite adhesives. The results indicated that by incorporating silanized silica fume to the epoxy based adhesives, the pull-out strength and displacement (i.e. toughness) incredibly increased. This was corresponded to the good interactions between modified silica fume with epoxy chains that prepared a nanocomposite adhesive with homogeneous dispersion of nanoparticles. This led the nanoparticles to diffuse into the micro/nano pores and cracks of concrete and increase in the steel rebar-concrete mechanical bonding. This also was related to the high toughness of the modified nanocomposite that increased its capability for damping the stresses.

Pull-out properties of anchoring systems; (a) strength/displacement and (b) pullout energy.

In the case of using fumed silica in epoxy resin, no influences were seen in the adhesion properties. This was related to two different phenomena that occurred in the sample which counteracted the effects. In one hand, silica fume improved the mechanical properties of epoxy adhesive. In the other hand, the agglomerated nanoparticles at the interface of epoxy resin and concrete/steel surfaces decreased their effective contact area that could cause creation of micro cracks and fracture under pullout stress.

Figure 4S in supporting information shows comparative pullout load–displacement curves of the adhesives. It is clearly seen that rebar pulled out completely from the hole. The highest end displacement content is less than 8 mm.

Figure 9b shows the adhesion energy/toughness of the adhesives (i.e. based on the measured area under pullout load–displacement curves). It is obvious that pure silica nanoparticles improved toughness of the pristine adhesive layer but modified nanoparticles enhanced it incredibly.

The significant increment in the bonding strength of modified nanocomposite adhesive to concrete/steel rebar surfaces should be corresponded to its different bonding mechanism. The present epoxide groups on the surface of silanized silica fume could react directly to amine groups of the curing agent. They also could react to the OH groups that created by epoxide rings opening through curing reactions. These covalent bonds increase the toughness and strength of the adhesive (see Fig. 10a). The hydrophobic nature of the modified adhesive prohibits accumulation of water at the interface of concrete and adhesive that usually happens during moisture exchange of hydrophilic concrete and decreases its interfacial interactions54.

(a) Schematic of bonding mechanism of modified nanoparticles to epoxy resin via co-curing process, (b) images from surface of pulled out steel rebar from concrete for different samples, (c) surface images from concrete surface separated from steel rebar.

On this basis, it could be claimed that the modified adhesive could decrease the corrosion rate of the steel rebar due to resistance against diffusion of water (i.e. as steel corrosive agent). Figure 10b exhibits images from the pulled out steel rebar surface. It is evidently seen that pristine adhesive showed cohesion defect in concrete phase. This means that the strength of concrete bulk is lower than adhesion strength of rebar-adhesive-concrete system55.

In contrary, by using pure nano silica in epoxy adhesive, the cohesion defect transferred to the adhesive layer that indicates lower strength of the adhesive. The modified nanoparticles improved adhesive interfacial interactions to the steel rebar and concrete. It also strengthened the adjacent concrete layer (i.e. due to diffusion into the surface crack and pores of concrete that increased volume of the adhered concrete to the steel rebar after pullout test).

Figure 10c shows few pristine adhesive patches on the surface of concrete. This means that it had better adhesion to the steel surface than concrete. In contrast, in the case of using silica fume containing adhesive, much more adhesive patches was seen on the concrete surface that means cohesion fracture of the adhesive layer due to its weakness. In the case of using modified adhesive, massive groves appeared at the concrete surface that created due to improved interfacial adhesion and cohesion fracture in the concrete bulk instead of adhesive layer.

In this work, nano SiO2-epoxy adhesives were prepared for anchoring of steel rebar in concrete. The nanoparticles were firstly surface modified using an epoxy based silane to enhance their interfacial interactions to epoxy binder. The pullout adhesion test was performed for evaluation of adhesives performances. Based on the results the following conclusions were obtained:

It was found that the highest silane grafting content was achieved at silane concentration of 10X (i.e. 10 times to stoichiometric concentration) and the surface modification had no effect on the crystalline phase of nanoparticles but decreased their sizes.

Surface modification of nano silica caused increment in the WCA of epoxy film about 19 and 67% compared to the pristine epoxy and pure nanoparticle containing epoxy adhesives, respectively. It also changed the nature of the modified nanocomposite adhesive from hydrophilic to hydrophobic.

Addition of the pure nano silica (1 wt%) to epoxy matrix caused 56, 81, 200 and 66% increment in the tensile strength, tensile modulus, compressive strength and compressive modulus improved by 56, 81, 200 and 66%, respectively.

Incorporating 1 wt% of modified nano silica to epoxy adhesive caused 70, 20, 17 and 21% increment in the tensile strength, tensile modulus, compressive strength and compressive modulus compared to the epoxy adhesive filled by pure nano silica.

Modified nano silica caused 16 and 43% increment in the storage modulus of the epoxy nanocomposite compared to the pristine epoxy and pure nano silica containing adhesives, respectively. It also increased 6 and 10% the loss function (tanδ), respectively.

Using surface modified nano silica in epoxy matrix caused about 40 and 25% improvement in the pullout strength and 33 and 18% increment in the pullout displacement compared to the pristine epoxy and pure nano silica containing adhesives. The adhesion energy was enhanced up to 50 and 130% compared to the pure epoxy nanocomposite and pristine epoxy adhesives.

It is confirmed that all Data Availability. The raw/processed data required to reproduce these findings can be shared.

Bribián, I. Z., Capilla, A. V. & Usón, A. A. Life cycle assessment of building materials: Comparative analysis of energy and environmental impacts and evaluation of the eco-efficiency improvement potential. Build. Environ. 46(5), 1133–1140 (2011).

Article Google Scholar

Rehman, S. K. U., Ibrahim, Z., Memon, S. A. & Jameel, M. Nondestructive test methods for concrete bridges: A review. Constr. Build. Mater. 107, 58–86 (2016).

Article Google Scholar

Li, Z., Zhou, X., Ma, H. & Hou, D. Advanced Concrete Technology (John Wiley & Sons, 2022).

Book Google Scholar

Brandt, A. M. Fibre reinforced cement-based (FRC) composites after over 40 years of development in building and civil engineering. Compos. Struct. 86(1–3), 3–9 (2008).

Article Google Scholar

Xue, J. et al. Severely damaged reinforced concrete circular columns repaired by turned steel rebar and high-performance concrete jacketing with steel or polymer fibers. Appl. Sci. 8(9), 1671 (2018).

Article Google Scholar

Hosseini, F. & Gencturk, B. Structural assessment of bridge columns with engineered cementitious composites and Cu–Al–Mn superelastic alloys. Constr. Build. Mater. 203, 331–342 (2019).

Article CAS Google Scholar

Xing, Y., Wang, W., Ou, Y., Jiang, X. & Al-azzani, H. Seismic behavior of steel truss and concrete composite shear wall with double X-shaped braces. J. Build. Eng. 62, 105399 (2022).

Article Google Scholar

Guo, C. et al. The ability of biodegradable thermosensitive hydrogel composite calcium-silicon-based bioactive bone cement in promoting osteogenesis and repairing rabbit distal femoral defects. Polymers 14(18), 3852 (2022).

Article CAS PubMed PubMed Central Google Scholar

Hojati, M. et al. Barbed-wire reinforcement for 3D concrete printing. Autom. Constr. 141, 104438 (2022).

Article Google Scholar

Gebhard, L., Esposito, L., Menna, C. & Mata-Falcón, J. Inter-laboratory study on the influence of 3D concrete printing set-ups on the bond behaviour of various reinforcements. Cement Concr. Compos. 133, 104660 (2022).

Article CAS Google Scholar

Zhao, J., Mei, K. & Wu, J. Long-term mechanical properties of FRP tendon–anchor systems: A review. Constr. Build. Mater. 230, 117017 (2020).

Article CAS Google Scholar

Duo, Y., Liu, X., Liu, Y., Tafsirojjaman, T. & Sabbrojjaman, M. Environmental impact on the durability of FRP reinforcing bars. J. Build. Eng. 43, 102909 (2021).

Article Google Scholar

Ghayeb, H. H., Razak, H. A. & Sulong, N. R. Performance of dowel beam-to-column connections for precast concrete systems under seismic loads: A review. Constr. Build. Mater. 237, 117582 (2020).

Article Google Scholar

Qureshi, T. et al. Graphene-based anti-corrosive coating on steel for reinforced concrete infrastructure applications: Challenges and potential. Constr. Build. Mater. 351, 128947 (2022).

Article CAS Google Scholar

Alwash, D., Kalfat, R., Al-Mahaidi, R. & Du, H. Shear strengthening of RC beams using NSM CFRP bonded using cement-based adhesive. Constr. Build. Mater. 301, 124365 (2021).

Article CAS Google Scholar

Harilal, M. et al. The chloride-induced corrosion of a fly ash concrete with nanoparticles and corrosion inhibitor. Constr. Build. Mater. 274, 122097 (2021).

Article CAS Google Scholar

Effiong, J. U. & Ede, A. N. Experimental investigation on the strengthening of reinforced concrete beams using externally bonded and near-surface mounted natural fibre reinforced polymer composites: A review. Materials 15(17), 5848 (2022).

Article ADS CAS PubMed PubMed Central Google Scholar

Choo, Y. J., Lee, G. H., Lee, S.-J. & Park, C.-G. Effects of wollastonite fiber and styrene-butadiene latex polymer on the long-term durability of cement-based repair materials. Materials 15(15), 5433 (2022).

Article ADS CAS PubMed PubMed Central Google Scholar

Modesti, L. A., de Vargas, A. S. & Schneider, E. L. Repairing concrete with epoxy adhesives. Int. J. Adhes. Adhes. 101, 102645 (2020).

Article CAS Google Scholar

Bazli, M., Heitzmann, M. & Hernandez, B. V. Hybrid fibre reinforced polymer and seawater sea sand concrete structures: A systematic review on short-term and long-term structural performance. Constr. Build. Mater. 301, 124335 (2021).

Article Google Scholar

Marques, A. C. et al. Review on adhesives and surface treatments for structural applications: Recent developments on sustainability and implementation for metal and composite substrates. Materials. 13(24), 5590 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Moosavi, M., Jafari, A. & Khosravi, A. Bond of cement grouted reinforcing bars under constant radial pressure. Cement Concr. Compos. 27(1), 103–109 (2005).

Article CAS Google Scholar

Chen, J., Liu, J., Hu, P., Sun, H. & Hu, X. Experimental and numerical investigation on seismic behavior of detachable precast concrete column joints with bolted flange plate. J. Build. Eng. 49, 104077 (2022).

Article Google Scholar

He, Y., Zhang, X., Hooton, R. & Zhang, X. Effects of interface roughness and interface adhesion on new-to-old concrete bonding. Constr. Build. Mater. 151, 582–590 (2017).

Article Google Scholar

Nodehi, M. Epoxy, polyester and vinyl ester based polymer concrete: a review. Innov. Infrastruct. Solut. 7(1), 1–24 (2022).

Article MathSciNet Google Scholar

Bloxham, J. W. Investigation of the Flexural Properties of Reinforced Concrete Beams Strengthened by Externally Bonded Steel Plates (University of Sheffield, 1980).

Google Scholar

Van Gemert, D. & Maesschalck, R. Structural repair of a reinforced concrete plate by epoxy bonded external reinforcement. Int. J. Cem. Compos. Lightweight Concrete 5(4), 247–255 (1983).

Article Google Scholar

Swamy, R. & Koyama, S. Epoxy coated rebars the panacea for steel corrosion in concrete. Constr. Build. Mater. 3(2), 86–91 (1989).

Article Google Scholar

Güneyisi, E., Gesoğlu, M., Akoi, A. O. M. & Mermerdaş, K. Combined effect of steel fiber and metakaolin incorporation on mechanical properties of concrete. Compos. B Eng. 56, 83–91 (2014).

Article Google Scholar

Agarwal, A., Nanda, B. & Maity, D. Experimental investigation on chemically treated bamboo reinforced concrete beams and columns. Constr. Build. Mater. 71, 610–617 (2014).

Article Google Scholar

Mahadik, V., Sharma, A. & Hofmann, J. Re-evaluation of existing tests on RC connections using post-installed reinforcing bars. Eng. Struct. 209, 109970 (2020).

Article Google Scholar

Khaksefidi, S., Ghalehnovi, M. & De Brito, J. Bond behaviour of high-strength steel rebars in normal (NSC) and ultra-high performance concrete (UHPC). J. Build. Eng. 33, 101592 (2021).

Article Google Scholar

Zhao, G. & Li, A. Numerical study of a bonded steel and concrete composite beam. Comput. Struct. 86(19–20), 1830–1838 (2008).

Article Google Scholar

Tan, F., Qiao, X., Chen, J. & Wang, H. Effects of coupling agents on the properties of epoxy-based electrically conductive adhesives. Int. J. Adhes. Adhes. 26(6), 406–413 (2006).

Article CAS Google Scholar

Li, G. et al. Tailored surface chemistry of SiO2 particles with improved rheological, thermal-mechanical and adhesive properties of epoxy based composites for underfill applications. Polymer 156, 111–120 (2018).

Article CAS Google Scholar

Al-Saleh, S. et al. Influence of TiO2 and ZrO2 nanoparticles on adhesive bond strength and viscosity of dentin polymer: A physical and chemical evaluation. Polymers 13(21), 3794 (2021).

Article CAS PubMed PubMed Central Google Scholar

Ghamarpoor, R. & Jamshidi, M. Synthesis of vinyl-based silica nanoparticles by sol–gel method and their influences on network microstructure and dynamic mechanical properties of nitrile rubber nanocomposites. Sci. Rep. 12(1), 1–15 (2022).

Article Google Scholar

Biuk Afshari, B., Jamshidi, M., Rostami, M. & Ghamarpoor, R. Improving the Mechanical/Anticorrosive Properties of a Nitrile Rubber-Based Adhesive Filled with Cerium Oxide Nanoparticles Using a Two-Step Surface Modification Method (ACS Omega, 2022).

Book Google Scholar

Gonçalves, F. A., Santos, M., Cernadas, T., Alves, P. & Ferreira, P. Influence of fillers on epoxy resins properties: A review. J. Mater. Sci. 57(32), 15183–15212 (2022).

Article ADS Google Scholar

Szymanowski, J. & Sadowski, Ł. The influence of the addition of tetragonal crystalline titanium oxide nanoparticles on the adhesive and functional properties of layered cementitious composites. Compos. Struct. 233, 111636 (2020).

Article Google Scholar

Ismael, R. et al. Influence of nano-SiO2 and nano-Al2O3 additions on steel-to-concrete bonding. Constr. Build. Mater. 125, 1080–1092 (2016).

Article CAS Google Scholar

May, M., Wang, H. & Akid, R. Effects of the addition of inorganic nanoparticles on the adhesive strength of a hybrid sol–gel epoxy system. Int. J. Adhes. Adhes. 30(6), 505–512 (2010).

Article CAS Google Scholar

Li, R. et al. Design of SiO2/PMHS hybrid nanocomposite for surface treatment of cement-based materials. Cement Concr. Compos. 87, 89–97 (2018).

Article CAS Google Scholar

Bagherzadeh, A., Jamshidi, M. & Monemian, F. Investigating mechanical and bonding properties of micro/nano filler containing epoxy adhesives for anchoring steel bar in concrete. Constr. Build. Mater. 240, 117979 (2020).

Article CAS Google Scholar

Mrkoci, M. I. Influence of Silica Surface Characteristics on Elastomer Reinforcement (Queen’s University, 2001).

Google Scholar

Ghamarpoor, R. & Jamshidi, M. Preparation of Superhydrophobic/Superoleophilic nitrile rubber (NBR) nanocomposites contained silanized nano silica for efficient oil/water separation. Sep. Purif. Technol. 291, 120854 (2022).

Article CAS Google Scholar

Ghamarpoor, R. & Silanizing, J. M. Nano SiO2 and its application in recycled nitrile rubber to prepare super oil resistant/superhydrophobic/superoleophilic oil/water separator. J Environ Chem Eng 10(3), 107971 (2022).

Article CAS Google Scholar

Ghamarpoor, R. & Jamshidi, M. Synergistic effect of microwave assisted devulcanization of waste NBR rubber and using superhydrophobic/superoleophilic silica nanoparticles on oil-water separation. Alex. Eng. J. 69, 67–84 (2023).

Article Google Scholar

Grell, J., Bernstein, J. & Tinhofer, G. Graph-set analysis of hydrogen-bond patterns: some mathematical concepts. Acta Crystallogr. B 55(6), 1030–1043 (1999).

Article CAS PubMed Google Scholar

Patterson, A. The Scherrer formula for X-ray particle size determination. Phys. Rev. 56(10), 978 (1939).

Article ADS CAS MATH Google Scholar

Eftekharipour, F., Jamshidi, M. & Ghamarpoor, R. Fabricating core-shell of silane modified nano ZnO: Effects on photocatalytic degradation of benzene in air using acrylic nanocomposite. Alex. Eng. J. 70, 273–288 (2023).

Article Google Scholar

Das, S., Halder, S., Paul, B., Khan, N. I. & Goyat, M. Impact of silanized milled graphite nanoparticles on thermo-mechanical properties of epoxy nanocomposite. Mater. Chem. Phys. 278, 125601 (2022).

Article CAS Google Scholar

Hagita, K. & Morita, H. Effects of polymer/filler interactions on glass transition temperatures of filler-filled polymer nanocomposites. Polymer 178, 121615 (2019).

Article CAS Google Scholar

Cui, C. & Liu, W. Recent advances in wet adhesives: Adhesion mechanism, design principle and applications. Prog. Polym. Sci. 116, 101388 (2021).

Article CAS Google Scholar

Ahmed, K. S., Shahjalal, M., Siddique, T. A. & Keng, A. K. Bond strength of post-installed high strength deformed rebar in concrete. Case Stud. Constr. Mater. 15, e00581 (2021).

Google Scholar

Download references

Constructional Polymers and Composites Research Lab., School of Chemical, Petroleum and Gas Engineering, Iran University of Science and Technology (IUST), Tehran, Iran

Reza Ghamarpoor, Masoud Jamshidi & Majid Mohammadpour

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

R.G.: Conceptualization, methodology, investigation, data curation, writing—original draft. M.J.: Conceptualization, methodology, validation, resources, data curation. M.M.: Methodology, investigation.

Correspondence to Masoud Jamshidi.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Ghamarpoor, R., Jamshidi, M. & Mohammadpour, M. Achieving outstanding mechanical/bonding performances by epoxy nanocomposite as concrete–steel rebar adhesive using silane modification of nano SiO2. Sci Rep 13, 9157 (2023). https://doi.org/10.1038/s41598-023-36462-0

Download citation

Received: 28 March 2023

Accepted: 04 June 2023

Published: 06 June 2023

DOI: https://doi.org/10.1038/s41598-023-36462-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Scientific Reports (2023)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.